Mechanical properties and UV stability of poly(tetrafluoroethylene) powder filled low density polyethylene

Download
076070.pdf
1998
Akınay, Ali Erkan
Show full item record
128
views
0
downloads
Polyethylene, Polymers and polymer manufacture, Chemical technology
https://hdl.handle.net/11511/1837
Graduate School of Natural and Applied Sciences, Thesis

Suggestions

Thermal characterization of phenol and bisphenol-A based polybenzoxazines
Bagherifam, Shahla; Hacaloğlu, Jale; Department of Polymer Science and Technology (2009)
Although, several researches on synthesis and characterization of benzoxazines and polybenzoxazines have appeared in the literature, detailed studies on thermal characterization are still limited. In this study, polymerization and thermal degradation mechanisms of benzoxazines were investigated via direct pyrolysis mass spectrometry. Benzoxazine monomers prepared by reactions of phenol or bisphenol- A with aniline or methyl amine were analyzed to investigate the effects of the structures of phenyl and amine...
Electrochemical synthesis of crowned conducting polymers : nature of radical cations in polymerization and mechanism of conductivity
Cihaner, Atilla; Önal, Ahmet Muhtar; Department of Chemistry (2004)
Poly(dibenzo-18-crown-6) (Poly(DB18C6)) was synthesized by electrochemical oxidation of dibenzo-18-crown-6 (DB18C6) using a mixture of acetonitrile and dichloromethane as solvent and tetrabutylammonium tetrafluoroborate (TBABF4) or tetrabutylammonium hexafluorophosphate (TBAPF6) as supporting electrolyte. The anodic polymerization of DB18C6 was investigated using in-situ ESR and in-situ UV-VIS spectroscopic techniques. Spectroelectrochemical (SPEL) properties and thermal analysis of the resulting polymers h...
Polymerization and polymer characterization of n-vinylcaprolactam
Polat, Özlem; Usanmaz, Ali; Department of Polymer Science and Technology (2005)
In this study, N-vinylcaprolactam was polymerized by radiation in the solid state. The polymerization was carried out at room temperayure under vacuum and open to atmosphere respectively. The polymerization mechanism showed autoacceleration and the rate of polymerization was higher in the presence of oxygen. However the limiting conversion was 100% under vacuum conditions and 90% in the present of oxygen. This is due to the low molecular weight olgomer formation in the presence of oxygen. The polymers were ...
THERMAL POLYMERIZATION OF BIS(TRIHALOPHENOXO)COPPER(II) COMPLEXES IN EXCESS DIMETHYLFORMAMIDE AND DIMETHYL-SULFOXIDE AS LIGANDS
KISAKUREK, D; SANLI, O (1989-08-01)
Thermal decomposition of bis(trihalophenoxo)copper(II) complexes was achieved at 50°C in dimethylformamide or dimethyl sulfoxide. The resulting polymers, poly(oxydihalophenylene)s (2), were characterized by FTIR, 1H NMR and 13C NMR spectroscopy and by differential scanning calorimetry. The molecular weights were determined by the vapour pressure method. Tribrominated phenol derivatives prefer 1,4‐substitution, whereas with trichlorophenol derivatives 1,2‐and 1,4‐substitutions take place at equal rates in ei...
Mechanical properties of plasma surface-modified calcium carbonate-polypropylene composites
Akovali, G; Akman, MA (Wiley, 1997-02-01)
Calcium carbonate was surface-modified by plasma-polymerized acetylene and the effect of surface modification on the mechanical properties of calcium carbonate-polypropylene composites was investigated. Two different plasma polymerization conditions were selected and applied. Chemical structures of plasma-polymerized acetylene products were identified. Mechanical and thermal properties of the composites prepared were evaluated and the effects of surface modification on the extent of adhesion of filler to th...
Citation Formats
A. E. Akınay, “Mechanical properties and UV stability of poly(tetrafluoroethylene) powder filled low density polyethylene,” Ph.D. - Doctoral Program, Middle East Technical University, 1998.
METU IIS - Integrated Information Service open@metu.edu.tr