COLLECTORLESS FLOTATION OF DEREKOY-SEBINKARAHISAR/GIRESUN LEAD AND ZINC-SULFIDE ORE WITH SODIUM SULFIDE

Date

1994-09-08

Author

HICYILMAZ, C
CEYLAN, H

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

100
views

0
downloads

A study on collectorless flotation of lead and zinc sulphide present in the Derekoy ore in the presence of sodium sulphide was performed. The parameters of the process and influence of sodium sulphide, zinc sulphide, conditioning time, pH and cleaning of concentrate were investigated. The results were compared with collector added flotation using several types of collectors.

Subject Keywords

Flotation, Galena , Zinc Sulphide, Conditioning Time, PH

URI

https://hdl.handle.net/11511/65521

Collections

Department of Mining Engineering, Conference / Seminar

Suggestions

OpenMETU
Core

Recovery of copper from oxide copper ore by flotation and leaching Kiraz, Emirhan; Atalay, Mustafa Ümit; Department of Mining Engineering (2014) The aim of this study was the recovery of copper from the oxide copper ore by froth flotation and agitating sulphuric acid (H2SO4) leaching. The ore with 4.21% copper grade used in this study was obtained from Çorum-Dangaz region of Turkey. Native copper, cuprite (Cu2O), tenorite (CuO), and malachite (Cu2(OH)2/CO3) were the main copper minerals in the test sample. Quartz, calcite, illite, chlorite, and plagioclase were determined as the main gangue minerals of the sample. The mesh of grind size of copper mi...
Synthesis and characterization of copper phthalocyanine deposited mica titania pigment Topuz, Berna Burcu; Gündüz, Güngör; Department of Polymer Science and Technology (2010) In the present work, anatase and rutile titanium dioxide (TiO2) coated lustrous mica pigments were prepared by heterogeneous nucleation method. Anatase-rutile phase transformation of the TiO2 on mica substrate was achieved by coating very thin layers of tin (IV) oxide on mica surfaces prior to TiO2 deposition. Muscovite mica, which was used in the experiments was sieved, pre-treated with sodium bicarbonate and decantated before coating process. The surface morphology of mica titania pigments and anatase-rut...
Pressure leaching of Sivrihisar-Yunus Emre nickel laterites Seçen, Berk; Topkaya, Yavuz Ali; Department of Metallurgical and Materials Engineering (2011) The aim of this thesis study was to extract nickel and cobalt from Sivrihisar limonitic nickel laterite ore by high pressure acid leaching (HPAL) method under most economical operating parameters. Optimizing the conditions to yield a saleable quality mixed hydroxide product from the pregnant leach solution (PLS) was also investigated. To extract high amounts of nickel and cobalt from the laterite matrix; leaching duration, leaching temperature and sulfuric acid/ore ratio were studied at fixed conditions of ...
Photocatalytic properties of silver loaded titanium dioxide powders produced by mechanical ball milling Aysin, Başak; Öztürk, Abdullah; Park, Jongee; Department of Metallurgical and Materials Engineering (2012) Silver (Ag) was loaded to three different kinds (P-25, NT-22, and TiO(OH)2) of titanium dioxide (TiO2) powders through adding three different quantities (4.6, 9.2, and 13.8 ml) of silver nitrate (AgNO3) solution by mechanical ball milling process. X-Ray diffraction analysis suggested that Ag was loaded on the TiO2 powders in the form of silver oxide (AgO). SEM, particle size, and BET surface area analyses revealed that TiO2 particles agglomerated after ball milling, resulting in the decrease of specific sur...
Pressure leaching of Çaldağ lateritic nickel ore Önal, Mehmet Ali Recai; Topkaya, Yavuz Ali; Department of Metallurgical and Materials Engineering (2013) The purpose of this study was to investigate the process optimization of combined high pressure acid leaching (HPAL) and mixed hydroxide precipitation (MHP) route for the extraction of nickel and cobalt from Çaldağ lateritic nickel ore. In order to extract nickel and cobalt values into pregnant leach solution (PLS), several process parameters of HPAL including acid load, temperature, leaching duration and particle size were investigated in comparative manner at constant solid concentration and agitation spe...

Citation Formats

C. HICYILMAZ and H. CEYLAN, “COLLECTORLESS FLOTATION OF DEREKOY-SEBINKARAHISAR/GIRESUN LEAD AND ZINC-SULFIDE ORE WITH SODIUM SULFIDE,” 1994, p. 121, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/65521.