Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
Fabrication of single-crystalline germanium with rapid-melting-growth
Date
2017-10-25
Author
Ayan, Arman
Özyutrt, İrem
Yerci, Selçuk
Metadata
Show full item record
Item Usage Stats
32
views
0
downloads
Cite This
URI
https://hdl.handle.net/11511/83405
Conference Name
NanoTR 2017 : 13th Nanoscience Nanotechnology Conference (22 - 25 Ekim 2017)
Collections
Unverified, Conference / Seminar
Suggestions
OpenMETU
Core
FABRICATION OF MIXED HALIDE PEROVSKITE FILMS BY THERMAL CO-EVAPORATION
Yılmaz, Onur; Yerci, Selçuk (2019-06-01)
Fabrication of CdSexTe1-x thin films by sequential growth using double sources
Demir, Medine; Terlemezoglu, M.; Parlak, Mehmet (2021-10-15)
CdSexTe(1-x) (CST) ternary thin films were fabricated by stacking thermally evaporated CdSe and electron beam evaporated CdTe layers. The final structure was achieved in a stoichiometric form of approximately Cd:Se:Te = 50:25:25. The post-annealing processes at 300, 400, and 450 °C were applied to trigger the compound formation of CST thin films. The X-ray diffraction (XRD) profiles revealed that CdTe and CdSe have major peaks at 23.9° and 25.5° corresponds to (111) direction in cubic zinc-blend structure. ...
Fabrication of alumina/polyimide multi-layered material by sputtering and vapor deposition polymerization
Naganuma, Tamaki; Kakisawa, Hideki; Dericioğlu, Arcan Fehmi; Kagawa, Yutaka (2006-08-01)
The alumina/polyimide multi-layers were fabricated by dry process using sputtering and vapor deposition polymerization. The alumina layer and polyamic acid layer as a polyimide precursor were coated on a Si substrate at room temperature. The layered structure was prepared under the continuous and discontinuous depositions; the former was to evaporate continuously under vacuum, while the latter was to expose in air after each layering process and to form the next layer under vacuum. After alternating deposit...
Fabrication and doping of thin crystalline Si films prepared by e-beam evaporation on glass substrate
Sedani, Salar Habibpur; Turan, Raşit; Ünalan, Hüsnü Emrah; Department of Micro and Nanotechnology (2013)
In this thesis study, fabrication and doping of silicon thin films prepared by electron beam evaporation equipped with effusion cells for solar cell applications have been investigated. Thin film amorphous Si (a-Si) layers have been fabricated by the electron beam evaporator and simultaneously doped with boron (B) and phosphorous (P) using effusion cells. Samples were prepared on glass substrates for the future solar cell operations. Following the deposition of a-Si thin film, crystallization of the films h...
Fabrication of various metal nanostructures with hole mask colloidal lithography
Öztürk, İbrahim Murat; Bek, Alpan; Department of Physics (2014)
In this work, a novel surface nanostructuring technique called hole mask colloidal lithography (HMCL) is investigated and utilized to fabricate large area metal nanostructures with several geometries with photoresist over exposure and over develop as the undercutting method. Some extends of this method has been examined with constant angled deposition of dimer structures. HMCL takes advantage of directional nature of thermal evaporation method for metal deposition through the nanoscale holes that are placed...