Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
Thermally controlled band gap tuning in CuO nano thin films for optoelectronic applications
Date
2024-01-01
Author
Delice, S.
Isik, M.
Hasanlı, Nızamı
Metadata
Show full item record
This work is licensed under a
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License
.
Item Usage Stats
4
views
0
downloads
Cite This
Temperature dependency of band gap in CuO nano thin films has been investigated by virtue of transmission experiments at different temperatures. Structural and morphological characterization were achieved using X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements. Analysis on the XRD diffractogram revealed the presence of monoclinic structure for the CuO. Average crystallite size was determined as 17.8 nm. Absorption characteristics in between 10 and 300 K were presented in the wavelength range of 360–1100 nm. The band gap of the CuO was found to be ~ 2.17 eV at 300 K using Tauc and spectral derivative methods. This value increased to ~ 2.24 eV at 10 K. Both methods showed that the band gap extended with decreasing temperature. Temperature dependency of the band gap was studied using Varshni relation. The band gap at absolute temperature, variation of the band gap with temperature and Debye temperature were calculated as 2.242 ± 0.002 eV, − 5.4 ± 0.2 × 10−4 eV/K and 394 ± 95 K, respectively.
Subject Keywords
Copper (II) oxide
,
Nanoparticles
,
Optical properties
,
Optoelectronics
,
Oxides
URI
https://hdl.handle.net/11511/109312
Journal
Indian Journal of Physics
DOI
https://doi.org/10.1007/s12648-024-03163-x
Collections
Department of Physics, Article
Citation Formats
IEEE
ACM
APA
CHICAGO
MLA
BibTeX
S. Delice, M. Isik, and N. Hasanlı, “Thermally controlled band gap tuning in CuO nano thin films for optoelectronic applications,”
Indian Journal of Physics
, pp. 0–0, 2024, Accessed: 00, 2024. [Online]. Available: https://hdl.handle.net/11511/109312.