The effect of various heat treating parameters on hardness and microstructures of the experimental 18% nickel maraging steels

Download

005284.pdf

Date

1988

Author

Pektaş, İlhami

Metadata

Show full item record

Item Usage Stats

68
views

0
downloads

URI

https://hdl.handle.net/11511/11098

Collections

Graduate School of Natural and Applied Sciences, Thesis

Suggestions

OpenMETU
Core

The effects of various heat treating parameters on the hardness and microstructures of the experimental 18% nickel maraging steels Pektas, I; Atala, H (1998-01-01) The effect of the parameters of heat treatment on the experimental 18% maraging steels was studied using hardness tester, optical, scanning electron and transmission electron microscopy and X-ray metallography techniques. The specimens were solution treated at 815, 900, 1000, 1060 degrees C for periods between 1 and 4 h. After air-cooling to room temperature. a bce martensitic structure was obtained. The higher temperature (1060 degrees C) and longer time (4 h) of the solution treatment caused essentially h...
The Effect of Strain Rate and Temperature on Forming Limit Diagram for DKP-6112 and AZ31 Materials Goksen, Seckin; Darendeliler, Haluk (2020-01-01)
The effect of strain rate and temperature on forming limit diagram for DKP-6112 and AZ31 materials Goksen, Seckin; Darendeliler, Haluk (2020-01-01) Forming limit diagrams (FLDs) are used in sheet metal operations widely for predicting blank fracture and forming characteristics of materials. There are three approaches for building forming limit diagrams which are the experimental, theoretical and numerical methods. Experimental method, which includes Nakazima formability test, is generally preferred for determining forming limit diagrams, although it requires complex experimental setup and effort. This study, firstly, compares the experimentally determi...
The effect of metallurgical factors on the abrasive wear resistance of AISI 1040, 4340 and 5140 steels Dikmen, Deniz; Atala, Haluk; Department of Metallurgical Engineering (1988)
The effect of retained austenite on the abrasive wear resistance of aisi 52100 steels Büget, Cem; Atala, Haluk; Department of Metallurgical Engineering (1993)

Citation Formats

İ. Pektaş, “The effect of various heat treating parameters on hardness and microstructures of the experimental 18% nickel maraging steels,” Middle East Technical University, 1988.