Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Open Access Guideline
Open Access Guideline
Postgraduate Thesis Guideline
Postgraduate Thesis Guideline
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
High temperature testing and analysis of crack growth in weldments.
Download
119057.pdf
Date
2002
Author
Ayhan, Ömer Talat
Metadata
Show full item record
Item Usage Stats
119
views
0
downloads
Cite This
URI
https://hdl.handle.net/11511/12705
Collections
Graduate School of Natural and Applied Sciences, Thesis
Suggestions
OpenMETU
Core
High temperature deformation behaviour of particle strengthened Fe-1%V alloy.
Akman, Oktay; Department of Metallurgical Engineering (1983)
High temperature bromination. Part 18: Bromination of benzonorbornadiene derivatives: Polybrominated benzonorbornenes and benzonorbornadienes
Dastan, A; Balcı, Metin (Elsevier BV, 2005-06-06)
The low and high temperature bromination reactions of bromobenzonorbornadiene derivatives were studied and the possible role of a neighboring group in rearrangements was investigated. New polybrominated benzonorbornadiene and benzonorbornene derivatives were synthesized. All compounds were characterized property Using NMR spectroscopy.
High temperature bromination. Part 12: Bromination of 7-oxabenzonorbornadiene: Synthesis of 2,3-dibromo-7-oxabenzonorbornadiene
Altundas, A; Dastan, A; McKee, MM; Balcı, Metin (Elsevier BV, 2000-08-11)
The electrophilic addition of bromine to 7-oxabenzonorbornadiene (8) at 0 degrees C led in high yield to the formation of dibromoaldehyde 10. However, high-temperature bromination of 8 in carbontetrachloride at 77 degrees C gave non-rearranged products 17 and 18. From the elimination of non-rearranged products, 2-bromo-7-oxabenzonorbornadiene (12) was obtained. Similarly, bromination of monobromide 12 at 77 degrees C yielded the non-rearranged tribromides 19 and 20 while bromination of 12 at 0 degrees C gav...
High temperature annealing of cold worked and nitrided 1 % V-Fe alloy.
Özdemir, A. Tamer; Department of Metallurgical Engineering (1984)
High temperature microstructural stability and recrystallization mechanisms in 14YWT alloys
Aydoğan Güngör, Eda; Takajo, S.; Vogel, S. C.; Maloy, S. A. (Elsevier BV, 2018-04-01)
In-situ neutron diffraction experiments were performed on room temperature compressed 14YWT nanostructured ferritic alloys at 1100 degrees C and 1150 degrees C to understand their thermally activated static recrystallization mechanisms. Existence of a high density of Y-Ti-O rich nano-oxides ( and {112} texture components during annealing, in contrast to the conventional recrystallization textures in body centered cubic alloys. Furthermore, nano-oxide size, shape, density and distribution are considerably di...
Citation Formats
IEEE
ACM
APA
CHICAGO
MLA
BibTeX
Ö. T. Ayhan, “High temperature testing and analysis of crack growth in weldments.,” Middle East Technical University, 2002.