Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Open Access Guideline
Open Access Guideline
Postgraduate Thesis Guideline
Postgraduate Thesis Guideline
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
Mode II fatigue crack growth behavior and mode II fracture toughness of 7050 aluminium alloy in two orientations
Download
index.pdf
Date
2013
Author
Yurtoğlu, M. Ender
Metadata
Show full item record
Item Usage Stats
126
views
99
downloads
Cite This
Fatigue crack growth behavior of AA7050 T7451 aluminum alloy under mode II loading condition in two orientations was investigated. Compact shear specimens were prepared in TL and LT directions. A loading frame for mode II type of loading was manufactured. Using the loading frame and the specimen, KIIC values and mode II fatigue crack growth rates were calculated. Fractographic analysis of the fracture surfaces of both mode II fracture toughness test specimens and mode II fatigue crack growth test specimens were done to examine the effects of mode II load. KIIC values were measured between 1.3 and 1.5 times the KIC values for this alloy. As for mode II fatigue crack growth rates, TL orientation shows the highest mode II fatigue crack growth resistance.
Subject Keywords
Fracture mechanics.
,
Deformations (Mechanics).
,
Strains and stresses.
,
Shear (Mechanics).
,
Aluminum alloys.
URI
http://etd.lib.metu.edu.tr/upload/12615581/index.pdf
https://hdl.handle.net/11511/22323
Collections
Graduate School of Natural and Applied Sciences, Thesis
Suggestions
OpenMETU
Core
CRACK-GROWTH KINETICS OF 7050-T73651 ALUMINUM-ALLOY UNDER CONSTANT LOAD AT 150-DEGREES-C
SARIOGLU, F; ABACHI, P; DORUK, M (Springer Science and Business Media LLC, 1993-03-15)
Crack growth tests at 150-degrees-C under constant load conditions were performed on compact tension specimens of 7050-T73651 aluminium alloy. The d.c. potential drop method was employed to monitor crack lengths throughout the tests. Fracture mechanics parameters such as the stress intensity factor (K) and energy-rate line integral (C*) were used to establish correlation with the crack propagation rates. As a result of experiments it was found that crack growth rates (da/dt) versus K, over discrete ranges o...
Three dimensional fracture analysis of FGM coatings under thermomechanical loading
Yildirim, B; Dağ, Serkan; Erdogan, E (Springer Science and Business Media LLC, 2005-04-01)
The main objective of this study is to examine the three dimensional surface crack problems in functionally graded coatings subjected to mode I mechanical or transient thermal loading. The surface cracks are assumed to have a semi-elliptical crack front profile of arbitrary aspect ratio. The cracks are embedded in the functionally graded material (FGM) coating which is perfectly bonded to a homogeneous substrate. A three dimensional finite element method is used to solve the thermal and structural problems....
Effect of retrogression and reaging heat treatment on corrosion fatigue crack growth behavior of AA7050 alloy
Akgün, Nevzat; Gürbüz, Rıza; Department of Metallurgical and Materials Engineering (2004)
The effect of retrogression and reaging heat treatment on corrosion fatigue crack growth behavior on AA7050 T73651 aluminum alloy is investigated. CT (Compact Tension) specimens are prepared in LS direction for fatigue crack growth tests . Samples are solution heat treated at 477 °C and aged at 120 °C for 24 h (T6 condition). After that, samples are retrogressed at 200 °C for times of 1, 5, 30, 55 and 80 minutes in a circulating oil bath. Then, samples are re-aged at 120 °C for 24 h (T6 condition). Hardness...
Shear mode fracture toughness of rock with different core-based specimen geometries
Het, Kıvanç; Tutluoğlu, Levend; Department of Mining Engineering (2014)
Shear mode fracture toughness tests on core specimens of gabbro rock were conducted. Tests were conducted under three-point bending and Brazilian type indirect compression load. In order to investigate the reasons for having different fracture toughness values with the different testing methods and geometries, modeling with ABAQUS software was conducted. Stress distributions around the mode II notches were analyzed. In order to assess which specimen geometry results in similar stress distributions as in the...
Effect of stress ratio on the rate of growth of fatigue cracks in 1100 Al-alloy
Bilir, Ömer.G.; Harun, Metin (Elsevier BV, 1990-1)
Axial load fatigue crack propagation tests were conducted on notched sheet specimens made of 1100 aluminum alloy. These tests were made at stress ratios (ratio of the minimum stress to the maximum stress) ranging from −0.5 to 0.5 in order to study the effects of stress ratio on fatigue crack growth. Experimental fatigue crack propagation data were analysed using Paris-Erdoǧan stress intensity analysis. The data from the tests at different stress ratios showed that two regions, namely, region I and region I...
Citation Formats
IEEE
ACM
APA
CHICAGO
MLA
BibTeX
M. E. Yurtoğlu, “Mode II fatigue crack growth behavior and mode II fracture toughness of 7050 aluminium alloy in two orientations,” M.S. - Master of Science, Middle East Technical University, 2013.