Preparation of B-ZSM-5 membranes on a monolith support

Date

2001-11-30

Author

Kalıpçılar, Halil
Noble, RD

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

218
views

0
downloads

A B-ZSM-5 zeolite membrane was synthesized on a monolith support containing 60 channels (2 mm x 2 mm.). The membrane showed a n-C4H10/i-C4H10 ideal selectivity at 373 K of 79 and a separation selectivity of 30.

Subject Keywords

Membrane preparation and structure, B-ZSM-5 membrane, Monolith support, Gas separations

URI

https://hdl.handle.net/11511/36252

Journal

JOURNAL OF MEMBRANE SCIENCE

DOI

https://doi.org/10.1016/s0376-7388(01)00594-4

Collections

Department of Chemical Engineering, Article

Suggestions

OpenMETU
Core

Synthesis and separation properties of B-ZSM-5 zeolite membranes on monolith supports Kalıpçılar, Halil; Noble, RD; Falconer, JL (2002-12-01) Alumina-coated, silicon carbide monoliths were used as supports for B-ZSM-5 zeolite membranes, which were synthesized by in situ hydrothermal crystallization. Both 2 turn x 2 mm (66 channels) and 4 mm x 4 mm (22 channels) monoliths with effective membrane area/volume ratios of 10.6 and 7.2 cm(2)/cm(3), respectively, were used. The membranes separated C-4 and C-6 hydrocarbon isomer vapor mixtures with high selectivities. The selectivities and permeances were comparable to tubular ZSM-5 membranes for butane i...
Preparation of MFI type zeolite membranes in a flow system with circulation of the synthesis solution Çulfaz Emecen, Pınar Zeynep; Kalıpçılar, Halil (2006-06-20) MFI type zeolite membranes were prepared on seeded tubular alumina supports in a flow system where the synthesis solution was circulated through the support with flow rates of 6, 24 and 48 mL/min. Syntheses were carried out using clear solutions, at 80 degrees C and 95 degrees C at atmospheric pressure in the flow system, and at autogeneous pressure in the batch system. The membranes synthesized in the flow system had thickness of 1-2 mu m, and were thinner than the membranes synthesized in the batch system...
Effect of preparation parameters on the performance of conductive composite gas separation membranes Gulsen, D; Hacarloglu, P; Toppare, Levent Kamil; Yılmaz, Levent (2001-02-15) Mixed matrix composite membranes of a conducting polymer, polypyrrole (PPy), and an insulating polymer, polybisphenol-A-carbonate (PC) were prepared by a combined in-situ polymerization and solvent evaporation. Mixed matrix composite membranes were synthesized to combine the good gas transport properties of conductive polymer, PPy, with good mechanical properties of PC.
Development of alumina supported ternary mixed matrix membranes for separation of H-2/light-alkane mixtures Topuz, Berna; Yılmaz, Levent; Kalıpçılar, Halil (2012-10-01) Ternary component mixed matrix membrane was prepared from PES, SAPO-34 and 2-hydroxy 5-methyl aniline on a macroporous alumina disk by the solvent evaporation method in order to investigate the effect of existence of an inorganic support. The membrane and its pure PES/Alumina counterpart were characterized by single gas permeability measurements of H-2, CH4, C2H6 and C3H8. The corresponding H-2/CH4 selectivities of membranes were 71.3 and 41. The membranes were also used to separate equimolar mixtures of H-...
GAS PERMEATION CHARACTERISTICS OF POLYMER-ZEOLITE MIXED MATRIX MEMBRANES SUER, MG; BAC, N; Yılmaz, Levent (1994-05-20) Mixed matrix membranes of polyethersulfone (PES), a glassy polymer, and hydrophilic zeolites 13X and 4A were prepared by using different membrane preparation procedures. Using selected procedure (c), the permeation rates of N2, O2, Ar, CO2 and H-2 were measured with a variety of membranes prepared at different zeolite loadings. Significant differences in measured permeability and calculated selectivity values demonstrated the importance of the type and percentage of zeolite. For both zeolitic additives, per...

Citation Formats

H. Kalıpçılar and R. Noble, “Preparation of B-ZSM-5 membranes on a monolith support,” JOURNAL OF MEMBRANE SCIENCE, pp. 141–144, 2001, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/36252.