Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Open Access Guideline
Open Access Guideline
Postgraduate Thesis Guideline
Postgraduate Thesis Guideline
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
Synthesis and characterization of Ba/MCM-41
Date
2010-01-01
Author
Kaya, Emine
Oktar, Nuray
Karakaş, Gürkan
Murtezaoglu, Kirali
Metadata
Show full item record
This work is licensed under a
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License
.
Item Usage Stats
212
views
0
downloads
Cite This
Mesoporous Ba/MCM-41 type materials (Ba/MCM-41) with high Ba/Si molar ratios between 0.025 and 0.1 were synthesized by direct hydrothermal synthesis. The samples were characterized by XRD, nitrogen adsorption, TGA-DTA, FTIR, SEM-EDS, and TEM techniques. BET surface areas of samples with various Ba loadings were found between 722 and 931 m(2)/g with 28 A average pore size, which is consistent with the pore size of 30 A for pure MCM-41 samples synthesized by the same procedure. The crystal structures of synthesized MCM-41 and Ba/MCM-41 were confirmed by XRD analysis. Among the investigated Ba/MCM-41 samples, the formation of barium oxide and barium nitrate species besides silicates was also observed in the high angle region XRD patterns.
Subject Keywords
MCM-41
,
Hydrothermal synthesis
URI
https://hdl.handle.net/11511/37645
Journal
TURKISH JOURNAL OF CHEMISTRY
DOI
https://doi.org/10.3906/kim-1003-2
Collections
Department of Chemical Engineering, Article
Suggestions
OpenMETU
Core
Synthesis and characterization of conducting copolymers of menthyl ester of 3-thiophene acetic acid with pyrrole
Kiralp, S; Alkan, S; Toppare, Levent Kamil; Cianga, I; Yagci, Y (2003-01-01)
A new thiophene derivative containing menthyl group (MM) was synthesized and polymerized via chemical and electrochemical (constant current) methods. Polymers obtained and MM itself were used to synthesize copolymers with pyrrole under conditions of constant potential electrolyses. Cyclic voltammetry (CV), thermal analysis (DSC, TGA) and scanning electron microscopy (SEM) analyses were performed for the characterization of samples.
Synthesis of Bishomoinositols and an Entry for Construction of a Substituted 3-Oxabicyclo[3.3.1]nonane Skeleton
BARAN, ARİF; Bekarlar, Merve; Aydin, Gokay; NEBİOĞLU, MEHMET; ŞAHİN, Ertan; Balcı, Metin (2012-02-03)
1,3,3a,7a-Tetrahydro-2-benzofuran was used as key compound for the synthesis of various bishomoinositol derivatives. The diene was subjected to an epoxidation reaction for further functionalization of the diene unit. The bisepoxide obtained was submitted to a ring-opening reaction with acid in the presence of water. Various bishomoinositols were synthesized. However, when the reaction was carried out in the presence of acetic anhydride, a substituted 3-oxabicyclo[3.3.1]nonane skeleton was formed. The mechan...
Synthesis, characterizations and investigation of thermoluminescence properties of strontium pyrophosphate doped with metals
Ilkay, L. S.; ÖZBAYOĞLU, GÜLHAN; Yılmaz, Ayşen (2014-11-01)
Strontium pyrophosphate, Sr2P2O7, was synthesized by solid-state synthesis method; the product was co-doped with copper-silver (Cu-Ag), copper-indium (Cu-In) and manganese-praseodymium (Mn-Pr) oxides (CuO, MnO, In2O3, Pr6O11 and AgNO3) by solid-state reaction method. The variation of dopant concentrations was investigated from 0.5 to 15% by weight. In addition to these processes, chemical characterizations of samples and the investigation of thermoluminescence (TLD) properties of strontium pyrophosphate wit...
Direct hydrothermal synthesis of palladium-incorporated silicate-structured mesoporous catalysts
Sener, Canan; Doğu, Timur; Dogu, Guelsen (2007-01-01)
Pd-Si-structured novel mesoporous nanocomposite catalytic materials, having quite high Pd/Si ratios, were synthesized by an acidic direct hydrothermal synthesis route. The nanocomposite catalytic materials were then characterized by XRD, XPS, EDS, nitrogen adsorption, and SEM techniques. Unlike MCM-41, the XRD patterns indicated a rather wide d((100)) band at a 2 theta value of about 1.9. The materials, with very high Pd/Si wt ratios between 1.43 and 2.66, were synthesized and had BJH surface area values be...
Synthesis and characterization of polythiophene/montmorillonite and polythiophene/polypropylene composites
Dülgerbaki, Çiğdem; Küçükyavuz, Zuhal; Department of Chemistry (2006)
In this study, polythiophene(PTP)/montmorillonite(MMT) nanocomposites were synthesized by in situ intercalative polymerization and chemical oxidative polymerization. In in situ intercalative polymerization method, composites containing 90 and 95% MMT were prepared. In chemical oxidative polymerization method, a series of composites ranging from 1 to 15% by weight MMT were synthesized. Thermal and morphological properties of samples were investigated by Differential Scanning Calorimeter (DSC), Thermal Gravim...
Citation Formats
IEEE
ACM
APA
CHICAGO
MLA
BibTeX
E. Kaya, N. Oktar, G. Karakaş, and K. Murtezaoglu, “Synthesis and characterization of Ba/MCM-41,”
TURKISH JOURNAL OF CHEMISTRY
, pp. 935–943, 2010, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/37645.