The effects of chlorine dioxide substitution for elemental chlorine in the chlorination stage, aimed at the minimization of chlorinated organics and subsequent oxygen reinforcement in the proceeding extraction stage on the characteristics of bleaching effluents have been examined. The characteristics of the effluents were assessed in terms of molecular weight distribution by gel filtration, so that alternatives for the treatment of these effluents can be proposed. The analysis of chlorination and extraction stage effluents with different chlorine dioxide substitution levels and varying available chlorine charges by using a Sephadex G-50 column have indicated that indeed a marked change in the molecular weight distribution of chlorinated organic compounds have occurred. The molecular size of chlorinated organic compounds in the chlorination stage has increased with the chlorine dioxide substitution, while that in the extraction stage has decreased when compared with the molecular size of these compounds in original bleaching effluents with only elemental chlorine used in the chlorination stage and followed by extraction stage. Molecular size of the chlorinated organic compounds in the chlorination stage effluents was not seriously affected by the chlorine dioxide substitution level; while ii was increased greatly by the increased total chlorine dosage. In the-extraction stage effluents, chlorine dioxide substitution level has not appeared to be an important parameter influencing the molecular size distribution. (C) 1997 IAWQ. Published by Elsevier Science Ltd.

Subject Keywords

Molecular weight distribution analysis, Gel filtration, Oxidative extraction, Chlorine dioxide, Pulp bleaching

URI

https://hdl.handle.net/11511/46609

Journal

WATER SCIENCE AND TECHNOLOGY

DOI

https://doi.org/10.1016/s0273-1223(97)00408-3

Collections

Department of Environmental Engineering, Article

Suggestions

OpenMETU
Core

Preparation and microstructure of sol-gel derived silver-doped silica Akkopru, Betul; Durucan, Caner (2007-08-01) Silver-doped silica was prepared by hydrolysis and condensation of tetraethyl orthosilicate (TEOS, Si(OC2H5)(4)) in the presence of a silver nitrate (AgNO3) solution by two different synthesis methods. In the first synthesis route, sol-gel mixtures were prepared using an acid catalyst. In the second synthesis route, silver-doped silica gels were formed by two-step acid/base catalysis. For the same concentration of silver dopant [AgNO3]/[TEOS] = 0.015 acid-catalyzed sol-gel formed a microporous silica with a...
Investigation of adsorption of pesticides by organo-zeolite from wastewater Lüle, Güzide Meltem; Atalay, M Ümit; Özbayoğlu, Gülhan; Department of Mining Engineering (2011) The aim of this study was to determine the adsorption capacity of activated carbon and organo-zeolites for removal of pesticides in water. In order to prepare organo-zeolite, two kinds of cationic surfactants, namely, hexadecyltrimethyl ammonium bromide (HTAB) and dodecyltrimethyl ammonium bromide (DTAB) were used. Adsorption studies of cationic surfactant on zeolite were investigated in respect to initial concentration of cationic surfactant, time, and temperature. It has been found that the best fitted is...
Characterization of nanostructured magnetite thin films produced by sol-gel processing Eken, Ali Erdem; Özenbaş, Ahmet Macit (2009-06-01) Nanocrystalline films of magnetite have been prepared by a novel sol-gel route in which, a solution of iron (III) nitrate dissolved in ethylene glycol was applied on glass substrates by spin coating. Coating solution showed Newtonian behaviour and viscosity was found as 0.0215 Pa.s. Annealing temperature was selected between 291 and 350 A degrees C by DTA analysis in order to obtain magnetite films. In-plane grazing angle XRD and TEM studies showed that magnetite phase was present upon annealing the films a...
Fabrication and characterization of porous hydroxyapatite and biphasic calcium phosphate ceramic as bone substitutes Koc, N; Timucin, M; Korkusuz, Feza (2004-01-01) In the present study, the calcium phosphate powders (HAP, HAP-TCP) were produced by a precipitation technique involving the use of aqueous solutions of calcium nitrate and diammonium hydrogen phosphate. Preforms of calcium phosphate ceramics were produced by using a modified slip casting technique. Porosity in the cast and in the sintered ceramic was obtained through custom made PMMA beads similar to200-300 mum size. The green ceramic samples were prepared by suspending the apatite powder and PMMA beads in ...
Characterization of magnetite thin films produced by sol-gel processing Eken, Ali Erdem; Özenbaş, Ahmet Macit; Department of Metallurgical and Materials Engineering (2008) Magnetite (Fe3O4) thin films were prepared by a sol-gel process in which, a solution of iron (III) nitrate dissolved in ethylene glycol was applied on glass substrates by spin coating. Xerogel films were obtained by drying the coated films at 110 °C. The films were sintered between 300 °C and 450 °C in order to observe the phases existing in the films at different temperatures. Coating solution showed Newtonian behaviour and viscosity was found as 0.0215 Pa.s. DTA analysis showed that, sintering temperature...

Citation Formats

Ü. Yetiş, C. Gokcay, and S. Sahin, “Characterization of effluents from chlorine dioxide substitution bleaching and oxygen-reinforced extraction,” WATER SCIENCE AND TECHNOLOGY, pp. 353–360, 1997, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/46609.