Effect of LiClO4 Salt on Dielectric Properties of Acrylonitrile-Methyl Methacrylate and Acrylonitrile-Isobutyl Methacrylate Copolymers

2014-01-01
VARGÜN, ELİF
ABACI, UFUK
SANKIR, MEHMET
Usanmaz, Ali
GÜNEY, HASAN YÜKSEL
Poly(acrylonitrile-co-isobutyl methacrylate), PAN-co-PIBMA, and poly(acrylonitrile-co-methyl methacrylate), PAN-co-MMA copolymers are synthesized by emulsion polymerization. The structural characterization is done by FTIR and H-1-NMR spectroscopy and thermal analyses are performed by thermogravimetric analysis (TGA). After various amounts of LiClO4 salt loading into copolymer films, the dielectric properties of these films at different temperatures and frequencies are determined. The effects of different methacrylate groups and salt content on the dielectric properties of copolymers are investigated. It is found that the dielectric constant increases systematically with increasing MMA and IBMA content in the copolymer. The samples with higher salt content show higher ac-conductivities.
JOURNAL OF MACROMOLECULAR SCIENCE PART A-PURE AND APPLIED CHEMISTRY

Suggestions

Preparation and characterization of acrylonitrile-ethyl methacrylate copolymers and the effect of LiClO4 salt on electrical properties of copolymer films
VARGÜN, ELİF; SANKIR, MEHMET; Usanmaz, Ali; Kanbur, Yasin; ABACI, UFUK; GÜNEY, HASAN YÜKSEL (2012-04-05)
Copolymers of poly(acrylonitrile-co-ethyl methacrylate), P(AN-EMA), with three different EMA content and parent homopolymers were synthesized by emulsion polymerization. The chemical composition of copolymers were identified by FTIR, H-1-NMR and C-13-NMR spectroscopy. The thermal properties of copolymers were modified by changing the EMA content in copolymer compositions. Various amounts of LiClO4 salt loaded (PAN-co-PEMA) copolymer films were prepared by solution casting. The dielectric properties of these...
Preparation and performance analysis of acrylonitrile based nanocomposite membranes for chromium (VI) removal from aqueous solutions
Bozkır, Selçuk; Usanmaz, Ali; Sankır, Mehmet; Department of Polymer Science and Technology (2010)
Acrylonitrile were copolymerized with 2-ethylhexyl acrylate and hexyl acrylate via one step emulsion polymerization using ammonium persulfate (initiator), 1-dodecanthiol (chain transfer agent) and DOWFAX 8390 (surfactant) in the presence of water at about 68 0C. Poly (acrylonitrile-2ethylhexyl acrylate) and poly (acrylonitrile-hexyl acrylate) copolymers with three different comonomer composition (8, 12 and 16 molar percent) were prepared. FTIR and 1H-NMR were used in order to clarify the chemical structure ...
Effect of W incorporation on the product distribution in steam reforming of bio-oil derived acetic acid over Ni based Zr-SBA-15 catalyst
Cakiryilmaz, Nurbanu; ARBAĞ, HÜSEYİN; OKTAR, NURAY; DOĞU, GÜLŞEN; Doğu, Timur (2018-02-15)
Zirconia incorporated SBA-15 type mesoporous material was synthesized following a one pot hydrothermal route, characterized and used as the catalyst support in the synthesis of Ni and bi-metallic Ni W based catalysts. Performances of these catalysts were tested in steam reforming of AcOH. Catalytic activity tests proved that the performances of SBA-15 and Zr-SBA-15 supported Ni based catalysts were highly stable and they also showed very high activity in steam reforming of acetic acid, giving complete conve...
Effect of sodium carbonate on carbothermic formation of hexagonal boron nitride
Akyıldız, Uğur; Sevinç, Naci; Department of Metallurgical and Materials Engineering (2010)
Effect of Na2CO3 on formation of hexagonal boron nitride (h-BN) by carbothermic method has been studied by subjecting B2O3-C and Na2CO3-added B2O3-C mixtures to N2 (g) atmosphere. Na2CO3 amount in the mixtures was changed in the range of 0-40 wt. %. Time and temperature were used as experimental variables. Reaction products were analyzed by XRD and scanning electron microscope. Na2CO3 was found to increase both the amount and the particle size of h-BN similar to CaCO3 [1]. Na2CO3 was found to be less effect...
Effect of impact modifier on the properties of poly (ethylene terephthalate)-organoclay nanocomposites
Yılmazer, Ülkü; Alyamac, Elif (2006-11-30)
The effects of component concentrations and addition order of the components, on the final properties of ternary nanocomposites composed of amorphous poly (ethylene terephthalate) matrix, organically modified clay, and an ethylene / methyl acrylate / glycidyl methacrylate (E-MAGMA) terpolymer were studied. All formulations were prepared by melt compounding of the components with a two-step mixing procedure in a corotating twin-screw extruder. Considering the X-Ray Diffraction, SEM, impact and strain at brea...
Citation Formats
E. VARGÜN, U. ABACI, M. SANKIR, A. Usanmaz, and H. Y. GÜNEY, “Effect of LiClO4 Salt on Dielectric Properties of Acrylonitrile-Methyl Methacrylate and Acrylonitrile-Isobutyl Methacrylate Copolymers,” JOURNAL OF MACROMOLECULAR SCIENCE PART A-PURE AND APPLIED CHEMISTRY, pp. 156–164, 2014, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/51657.