Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Open Access Guideline
Open Access Guideline
Postgraduate Thesis Guideline
Postgraduate Thesis Guideline
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
Effect of Cu addition on the microstructural constituents and mechanical properties of twin roll cast AlFeMnSi alloys
Date
2015-01-01
Author
Meydanoglu, Onur
Birbaşar, Onur
Ulus, Ali
Beyhan, Bariş
Kalay, Yunus Eren
Metadata
Show full item record
Item Usage Stats
190
views
0
downloads
Cite This
In this study, the effect of copper addition on microstructural evolution, mechanical and corrosion properties of twin roll cast (TRC) AlFeMnSi alloy system mainly used in container foil applications was investigated. Microstructural characterization studies were conducted on as-cast, homogenization annealed and final products by employing optical and scanning electron microscopes. The mechanical properties of the samples obtained from compositional were determined at the thickness of final product by tensile and Erichsen tests. Addition of Cu improved mechanical properties and formability performance of the foil products with the contribution of final annealing parameters. Corrosion properties were also improved as compared to those of the AlFeMnSi alloys having lower Cu content
Subject Keywords
AlFeMnSi alloys
,
Container foil
,
Homogenization
,
Twin roll casting
URI
https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84942898526&origin=inward
https://hdl.handle.net/11511/72824
Conference Name
Light Metals 2015 - TMS 2015 Annual Meeting and Exhibition (15 - 19 Mart 2015)
Collections
Department of Metallurgical and Materials Engineering, Conference / Seminar
Suggestions
OpenMETU
Core
Effect of surface treatment on electrical conductivity of carbon black filled conductive polymer composites
Koysuren, Ozcan; Yesil, Sertan; Bayram, Göknur (Wiley, 2007-06-05)
Two different types of surface modifiers, 3-aminopropyltriethoxysilane and formamide, were applied to carbon black (CB) particles to lower electrical resistivity of polymer composites prepared by treated CB. Two different matrices, low-density polyethylene and nylon 6, were chosen to compound with surface modified CB. Surface energy of CB was increased by adding amine or amide functional groups during surface treatment of CB. According to electron spectroscopy for chemical analysis (ESCA), chemical modifica...
Effect of swaging on microstructure and tensile properties of W-Ni-Fe alloys
DURLU, NURİ; Caliskan, N. Kaan; Bor, Sakir (Elsevier BV, 2014-01-01)
The objective of this study was to investigate the effect of swaging on the microstructure and tensile properties of high density two phase alloys 90W-7Ni-3Fe and 93W-4.9Ni-2.1Fe. Samples were liquid phase sintered under hydrogen and argon at 1480 degrees C for 30 min and then 15% cold rotary swaged. Measurement of microstructural parameters in the sintered and swaged samples showed that swaging slightly increased tungsten grain size in the longitudinal direction and slightly decreased tungsten grain size i...
Effect of expandable graphite on flame retardant, thermal and mechanical properties of thermoplastic polyurethane composites filled with huntite&hydromagnesite mineral
Guler, Turkan; Tayfun, Umit; Bayramlı, Erdal; DOĞAN, Mehmet (2017-01-10)
The effect of expandable graphite (EG) was studied on the flame retardant, thermal and mechanical properties of thermoplastic polyurethane (TPU) containing huntite&hydromagnesite (HH). According to the flammability tests results, the synergistic interaction was observed between HH and EG. The maximum limiting oxygen index (LOI value was observed at a ratio of 1:1 (HH:EG) and the highest vertical burning test (UL-94) rating of V0 was observed at a ratios of 4:1, 3:2 and 1:1. The synergistic interaction betwe...
Effects of Graphene Transfer and Thermal Annealing on Anticorrosive Properties of Stainless Steel
Oh, Jeong Hyeon; Han, Sangmok; Kim, Tae-Yoon; PARK, JONGEE; Öztürk, Abdullah; Kim, Soo Young (2017-11-01)
Stainless steel (STS) films were annealed in a thermal quartz tube and covered with graphene to improve their anticorrosive properties. Graphene was synthesized via the chemical vapor deposition method and transferred onto the surface of the STS film by the layer-by-layer approach. The structure of the STS film changed from alpha-Fe to gamma-Fe after annealing at 700 C for 1 h, resulting in an increase of 82.72% in the inhibition efficiency. However, one-layer graphene acted as a conductive pathway and ther...
Effect of microcapsulated red phosphorus on flame retardant, thermal and mechanical properties of thermoplastic polyurethane composites filled with huntite&hydromagnesite mineral
ATABEK SAVAŞ, Lemiye; Deniz, Tugba Kaya; Tayfun, Umit; DOĞAN, Mehmet (2017-01-01)
The effect of microcapsulated red phosphorus (mRP) was studied on the flame retardant, thermal and mechanical properties of thermoplastic polyurethane (TPU) composites containing Huntite&hydromagnesite (HH). The flame retardant properties of TPU based composites were investigated using limiting oxygen index (LOI), vertical burning test (UL 94), thermogravimetric analysis (TGA) and mass loss calorimeter. The mechanical properties of composites were studied using tensile test and dynamic mechanical analysis (...
Citation Formats
IEEE
ACM
APA
CHICAGO
MLA
BibTeX
O. Meydanoglu, O. Birbaşar, A. Ulus, B. Beyhan, and Y. E. Kalay, “Effect of Cu addition on the microstructural constituents and mechanical properties of twin roll cast AlFeMnSi alloys,” presented at the Light Metals 2015 - TMS 2015 Annual Meeting and Exhibition (15 - 19 Mart 2015), Florida, Amerika Birleşik Devletleri, 2015, Accessed: 00, 2021. [Online]. Available: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84942898526&origin=inward.