Production and Characterization of Yttria Stabilized Zirconia Ceramic Blocks for Dental Applications

2016-12-01
Kaplan, Melis
Park, Jongee
Öztürk, Abdullah
Show full item record
118
views
0
downloads
https://hdl.handle.net/11511/85234
18. Uluslararası Metalurji ve Malzeme Kongresi, (29 Eylül - 01 Ekim 2016)
Department of Metallurgical and Materials Engineering, Conference / Seminar

Suggestions

Production and characterization of yttria stabilized zirconia ceramic blocks for dental applications
Kaplan, Melis; Öztürk, Abdullah; Park, Jongee; Department of Metallurgical and Materials Engineering (2017)
Dense zirconia ceramic blocks were produced by pressureless sintering at temperatures down to 1350- 1450 oC for dental applications. The effect(s) of integration of cold isostatic pressing (CIP’ing) to the production procedure of the zirconia blocks was researched by applying 80, 100, and 150 MPa isostatic pressure. The effect of color infiltration solutions (NiCl2 and MoCl3 solutions) on color and low temperature degradation properties of zirconia was investigated. Tetragonal to monoclinic phase transforma...
Production and characterization of surface treated biomedical Ti6Al7Nb alloy foams /
Bütev, Ezgi; Bor, Şakir; Esen, Ziya; Department of Metallurgical and Materials Engineering (2015)
The current study was undertaken to investigate the production and surface processing of biomedical Ti6Al7Nb alloy foams. Space holder method was utilized to manufacture foams with varying porosities around 53.0-73.0 vol. % via evaporation of magnesium from compacted Ti6Al7Nb-Mg powder mixtures. Bioactivities of foam surfaces were further enhanced by obtaining sodium rich phases using NaOH alkali-heat treatment method. Moreover, untreated and surface treated foams were tested in simulated body fluid (SBF) i...
Production and properties of tooth-colored yttria stabilized zirconia ceramics for dental applications
Kaplan, Melis; PARK, JONGEE; Kim, Soo Young; Öztürk, Abdullah (Elsevier BV, 2018-02-01)
Dense zirconia stabilized with 3 mol% yttria ceramics were produced in disc shape by first cold isostatically pressing at 100 MPa and then sintering at 1450 degrees C at ambient laboratory conditions. Coloring was accomplished by immersion the discs in NiCl2, MoCl3, and NiCl2 + MoCl3 solutions for 5, 30, and 60 s. Different concentrations (0.1, 0.25, and 0.5 wt%) were applied to get the color of natural tooth. The density, color, microhardness, fracture toughness, compressive strength, and wear rate of the ...
Production and characterization of nano silver oxide for silver zinc batteries
Yurtseven, Özüm Öyküm; Aydınol, Mehmet Kadri; Nalbant Esentürk, Emren; Department of Micro and Nanotechnology (2013)
Rechargeable silver-zinc batteries have aroused interest and find various area of usage depending on their notably technical advantages over other battery systems including their high specific energy and high recharge efficiency. In this battery chemistry, silver oxide and metallic zinc are used as the positive and negative active materials respectively. Chemically stabilized particles with large surface areas are needed to reach high discharge rates for battery applications. The use of nanoparticles as ele...
Production and characterization of aluminum matrix-TIC composites by vacuum sintering
Seymen, Rıza Alparslan; Kalkanlı, Ali; Department of Metallurgical and Materials Engineering (1998)
Citation Formats
M. Kaplan, J. Park, and A. Öztürk, “Production and Characterization of Yttria Stabilized Zirconia Ceramic Blocks for Dental Applications,” presented at the 18. Uluslararası Metalurji ve Malzeme Kongresi, (29 Eylül - 01 Ekim 2016), 2016, Accessed: 00, 2021. [Online]. Available: https://hdl.handle.net/11511/85234.