Effect of resin and fiber on the abrasion, impact and pressure resistance of cylindrical composite structures

Download

index.pdf

Date

2011

Author

Kaya, Derya

Metadata

Show full item record

Item Usage Stats

263
views

173
downloads

The aim of this study was to investigate the effects of resin and fiber on the abrasion, impact and internal pressure resistances of fiber reinforced plastic composite pipes produced by continuous filament winding method. For this study, pipe samples were produced with different combinations of resin type, fiber type, fiber amount and fiber length. All the samples were tested in accordance with the related ISO (International Organization for Standardization), DIN (German Standardization Institution) and BSI (British Standards Institution) standards. Three types of resins were used as ortophthalic, isophthalic and vinylester; two types of fibers were used as E-glass and ECR-glass and one type of GLASSFLAKES was used as C-glass. It was observed that the type of resin did not have any significant effect on burst pressure. However, the vinylester resin had a considerable positive effect on the abrasion and impact resistances. Moreover, it was observed that the type of fiber did not have any significant effect on impact and internal pressure resistances, but the use of C-glass GLASSFLAKES resulted in a positive effect on the abrasion resistance. Additionally, it was found that the increase in the amount of glass fiber resulted in increase of burst pressure, impact and abrasion resistances. Finally, it was observed that the length of glass fiber did not have any significant effect on abrasion resistance, but the decrease in fiber length resulted in a higher internal pressure and impact resistances.

Subject Keywords

Composite materials.

URI

http://etd.lib.metu.edu.tr/upload/12613287/index.pdf
https://hdl.handle.net/11511/20642

Collections

Graduate School of Natural and Applied Sciences, Thesis

Suggestions

OpenMETU
Core

Effect of fiber and resin types on mechanical properties of fiber-reinforced composite pipe Gokce, Neslihan; Yılmazer, Ülkü; SUBAŞI, SERKAN (Thomas Telford Ltd., 2019-09-01) The aim of this study was to evaluate the effects of the types of fiber and resin on the mechanical properties of polyester composite pipes. Orthophthalic, isophthalic and vinyl ester resins were used as the matrix; E-glass, electrical/chemical resistance (ECR)-glass and basalt fibers were used as reinforcement; and 98% silica (SiO2) sand was used as filler in mixtures. Samples were produced by the centrifugal casting method. Samples cut from the produced pipes were tested to determine stiffness and longitu...
Effect of carbon nanotube surface treatment on the morphology, electrical, and mechanical properties of the microfiber-reinforced polyethylene/poly(ethylene terephthalate)/carbon nanotube composites Yesil, Sertan; Bayram, Göknur (2013-01-15) The aim of this study is to investigate the effects of carbon nanotube (CNT) chemical properties, CNT content, and molding temperature on the morphology, electrical, and mechanical properties of the microfiber-reinforced polymer composites. These composites were prepared by extrusion and hot stretching the poly(ethylene terephthalate) (PET)/CNT phase in high density polyethylene (HDPE) matrix. Surfaces of the CNT were modified by purification with strong acid mixture (HNO3 : H2SO4 mixture 1 : 1 by volume) f...
Effects of processing parameters on mechanical and thermal properties of glass mat reinforced nylon 6 composites Akkaoui, W; Bayram, Göknur (SAGE Publications, 2004-01-01) Nylon 6 (PA6)/Glass Mat (GM) composites and pure PA6 were prepared by compression molding technique and the effects of molding temperature, pressure application time and GM content on the final properties of the materials were investigated. At each temperature and pressure application time, the composite with one layer GM had higher tensile strength, tensile modulus but lower % elongation at break than neat PA6. Processing parameters did not significantly influence the tensile behavior of the pure PA6 and P...
Contribution of carbon nanotubes to vibration damping behavior of epoxy and its carbon fiber composites Avil, Esma; Kadioglu, Ferhat; Kaynak, Cevdet (SAGE Publications, 2020-04-01) The main objective of this study was to investigate contribution of the non-functionalized multi-walled carbon nanotubes on the vibration damping behavior of first neat epoxy resin and then unidirectional and bidirectional continuous carbon fiber reinforced epoxy matrix composites. Epoxy/carbon nanotubes nanocomposites were produced by ultrasonic solution mixing method, while the continuous carbon fiber reinforced composite laminates were obtained via resin-infusion technique. Vibration analysis data of the...
Production of epoxide functionalized boehmite nanoparticles and their use in epoxide nanocomposites Coniku, Anisa; Gündüz, Güngör; Maviş, Bora; Department of Chemical Engineering (2012) In the present study the effects of addition of organically functionalized boehmite nano-particles on the mechanical properties of epoxy polymers were analyzed. Nanosize platelets of boehmite powders were produced via a hydrothermal process from the raw material aluminum trihydroxide Al(OH)3 provided by a a chemical supplier, but which in future studies can be replaced by local resources of aluminum trihydroxide available in Seydişehir, Turkey. The ground aluminum trihydroxide particles were submitted to a ...

Citation Formats

D. Kaya, “Effect of resin and fiber on the abrasion, impact and pressure resistance of cylindrical composite structures,” M.S. - Master of Science, Middle East Technical University, 2011.