Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Open Access Guideline
Open Access Guideline
Postgraduate Thesis Guideline
Postgraduate Thesis Guideline
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
EFFECT OF ELECTROPLATING PARAMETERS ON "HER" CURRENT DENSITY IN Ni-MoS2 COMPOSITE PLATING
Date
2012-03-15
Author
Guler, Ebru Saraloglu
Karakaya, İshak
KONCA, ERKAN
Metadata
Show full item record
This work is licensed under a
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License
.
Item Usage Stats
206
views
0
downloads
Cite This
Nickel composites with co-deposited insoluble, solid lubricant particles such as MoS2 have been reported to reduce friction. It is known that hydrogen evolution reaction (HER), competes with nickel deposition. The influence of the electroplating parameters and their interaction effects on the peak current density for HER were studied by fractional factorial design. The parameters and their ranges were; MoS2 concentration (0-30 g/l), temperature (30-50 degrees C), pH (2-4) and surfactants (0-1 g/l). Electrodeposition processes were carried out from a typical Watts bath containing leveler, wetting agent and brightener by using a potentiostat. The peak currents (I-p) were extended to higher values and the peaks on linear sweep voltammograms became noticeable by increasing the scan rate from 20 mV/s to 100 mV/s over the range 0 to 2.5 V. The peak current densities (i(p)) for each experimental route were determined by fractional factorial design for three types of mineral processing surfactants; sodiumlignosulfonate (SLS), depramin-C (DC) and ammoniumlignosulfonate (ALS) using Minitab program [1]. Adding MoS2, decreasing temperature and increasing pH has decreasing effect on peak current density for all surfactants. ALS and DC have increasing effect whereas SLS has descending effect on peak current.
Subject Keywords
Electroco deposition
,
Voltammogram
,
Current density
URI
https://hdl.handle.net/11511/54936
Collections
Department of Metallurgical and Materials Engineering, Conference / Seminar
Suggestions
OpenMETU
Core
Effect of Electrodeposition Parameters on the Current Density of Hydrogen Evolution Reaction in Ni and Ni-MoS2 Composite Coatings
Gueler, E. Saraloglu; KONCA, ERKAN; Karakaya, İshak (2013-04-01)
Nickel composites with co-deposited insoluble, solid lubricant particles such as MoS2 have been reported to reduce friction. It is known that hydrogen evolution reaction (HER), competes with nickel deposition. The influence of the parameters and their interaction effects on the peak current density of HER during the electrodeposition of Ni and Ni-MoS2 composite coatings were studied by fractional factorial design. The parameters and their ranges studied were; MoS2 particle concentration (0-30 g/l), temperat...
Effect of expandable graphite on flame retardant, thermal and mechanical properties of thermoplastic polyurethane composites filled with huntite&hydromagnesite mineral
Guler, Turkan; Tayfun, Umit; Bayramlı, Erdal; DOĞAN, Mehmet (2017-01-10)
The effect of expandable graphite (EG) was studied on the flame retardant, thermal and mechanical properties of thermoplastic polyurethane (TPU) containing huntite&hydromagnesite (HH). According to the flammability tests results, the synergistic interaction was observed between HH and EG. The maximum limiting oxygen index (LOI value was observed at a ratio of 1:1 (HH:EG) and the highest vertical burning test (UL-94) rating of V0 was observed at a ratios of 4:1, 3:2 and 1:1. The synergistic interaction betwe...
Effect of carboxylic acid crosslinking of cellulose membranes on nanofiltration performance in ethanol and dimethylsulfoxide
Konca, Kubra; Çulfaz Emecen, Pınar Zeynep (2019-10-01)
Cellulose membranes were fabricated via phase inversion using 1-ethyl-3-methylimidazolium acetate as solvent and acetone as volatile cosolvent. 1,2,3,4-butanetetracarboxylic acid was used to partially crosslink the hydroxyl groups of cellulose, thereby changing mechanical properties of the membranes and the interactions with solvents, ethanol and dimethyl sulfoxide, and solutes. Rejection of dyes of similar size, Bromothymol Blue, Rose Bengal and Crystal Violet were shown to correlate inversely with sorptio...
Effect of surface treatment on electrical conductivity of carbon black filled conductive polymer composites
Koysuren, Ozcan; Yesil, Sertan; Bayram, Göknur (Wiley, 2007-06-05)
Two different types of surface modifiers, 3-aminopropyltriethoxysilane and formamide, were applied to carbon black (CB) particles to lower electrical resistivity of polymer composites prepared by treated CB. Two different matrices, low-density polyethylene and nylon 6, were chosen to compound with surface modified CB. Surface energy of CB was increased by adding amine or amide functional groups during surface treatment of CB. According to electron spectroscopy for chemical analysis (ESCA), chemical modifica...
Effect of cold rolling and annealing parameters on the microstructure and mechanical properties of dual phase steels
Poyraz, Okan; Ögel, Bilgehan; Department of Metallurgical and Materials Engineering (2020)
This study consists of change in the microstructure and mechanical properties of the 0.14C-1.98Mn steel with different cold rolling ratios, annealing temperature and annealing time. The starting sheet metal is 2.8mm thick and have a microstructure of ferrite-pearlite in as-received condition. Samples are cold rolled such that either 30%, 45% or 60% cold rolling is achieved. In order to see the change in microstructure below and in the intercritical temperatures, samples are annealed for 5 minutes or 10 minu...