Carboxyl‐terminated polybutadiene (CTPB) was subjected to temperature and humidity aging in order to estimate its useful lifetime as a solid propellant binder. CTPB samples were temperature aged from 1 week to 7 months at various temperatures ranging from 50 to 100°C. At various stages of temperature aging, viscosity of the samples were measured, end group analyses were performed, and the samples, after being crosslinked with MAPO, were mechanically tested. As far as mechanical properties are concerned, the ultimate tensile stress of the samples decreases with temperature aging and strain at break increases. End group analyses indicate that acid value of the samples decreases with aging and viscosity increases. The results of temperature aging were applied to an Arrhenius type time‐temperature superposition relation and useful lifetime of CTPB as binder at 20°C was predicted to be around 10 years. The CTPB samples were also humidity‐aged and the effects of humidity aging on mechanical properties were investigated. The results indicate that similar to temperature aging, ultimate tensile strength decreases and strain at break increases with aging. The effects of humidity aging, however, is much less pronounced in comparison to temperature aging.

Subject Keywords

Materials Chemistry, General Chemistry, Surfaces, Coatings and Films, Polymers and Plastics

URI

https://hdl.handle.net/11511/67670

Journal

JOURNAL OF APPLIED POLYMER SCIENCE

DOI

https://doi.org/10.1002/app.1991.070420118

Collections

Department of Chemical Engineering, Article

Suggestions

OpenMETU
Core

Curing characteristics of glycidyl azide polymer-based binders Kasikci, H; Pekel, F; Özkar, Saim (Wiley, 2001-04-04) The curing of a glycidyl azide polymer (GAP) with a triisocyanate, Desmodur N-100, was followed by measuring the hardness and viscosity. The thermal behavior of the cured samples were investigated by a differential scanning calorimeter (DSC) and thermal gravimetric analysis (TGA). Curing causes an increase in the glass transition temperature of GAP. The T-g of gumstocks also increases with an increasing NCO/OH ratio while the decomposition temperature remains practically unchanged. The ultimate hardness of ...
Thermal and mechanical properties of microwave- and heat-cured poly(methyl methacrylate) used as dental base material Usanmaz, Ali; Ates, J; Dogan, A (Wiley, 2003-10-03) The thermal and mechanical properties of dental base materials cured by microwave and conventional heat methods were studied. The commercial dental base poly(methvl metacrylate) (PMMA) powder and liquid were mixed in a 3/1 ratio. They were polymerized by a peroxy catalyst at 63degreesC, then cured with a boiling water temperature and microwave radiation for periods of 5, 10, 15, 20, 25, 30, and 35 min for heat curing and 1, 2, 3, 5, and 7 min for microwave radiation. The microwave radiation outputs used wer...
Thermal characterization of glycidyl azide polymer (GAP) and GAP-based binders for composite propellants Selim, K; Özkar, Saim; Yılmaz, Levent (Wiley, 2000-07-18) Differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) were used to investigate the thermal behavior of glycidyl azide polymer (GAP) and GAP-based binders, which are of potential interest for the development of high-performance energetic propellants. The glass transition temperature (T-g) and decomposition temperature (T-d) of pure GAP were found to be -45 and 242 degrees C, respectively. The energy released during decomposition (Delta H-d) was measured as 485 cal/g. The effect of th...
Hydroxyl-Terminated Poly(urethane acrylate) as a Soft Liner in Dental Applications: Synthesis and Characterization Keskin, Selda; Usanmaz, Ali (Wiley, 2010-07-05) Hydroxyl-terminated poly(urethane acrylate)s were synthesized for use in biomedical applications. Acrylate end capping via an interesterification reaction was successfully achieved with methacryloyl chloride addition to the hydroxyl ends of the polyurethane at low temperatures. 2,4-Toluene diisocyanate, 1,6-hexane diisocyanate, and methylene diphenyl diisocyanate were used as diisocyanates for urethane synthesis, and they were end-capped with methyl methacrylate and hydroxyethyl methacrylate. The nature of ...
Kinetics of polyurethane formation between glycidyl azide polymer and a triisocyanate Keskin, S; Özkar, Saim (Wiley, 2001-07-25) Kinetics of the polyurethane formation between glycidyl azide polymer (GAP) and a polyisocyanate, Desmodur N-100, were studied in the bulk state by using quantitative FTIR spectroscopy. The reaction was followed by monitoring the change in intensity of the absorption band at 2270 cm-l for NCO stretching in the IR spectrum, and was shown to obey second-order kinetics up to 50% conversion. The activation parameters were obtained from the evaluation of kinetic data at different temperatures in the range of 50-...

Citation Formats

F. BILGIN, T. SAGE, N. ORBEY, and O. GUVEN, “LIFETIME PREDICTION OF CARBOXYL-TERMINATED POLYBUTADIENE (CTPB),” JOURNAL OF APPLIED POLYMER SCIENCE, pp. 153–158, 1991, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/67670.