Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Open Access Guideline
Open Access Guideline
Postgraduate Thesis Guideline
Postgraduate Thesis Guideline
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
Characterization of TiO2 thin films prepared by sol-gel processing
Date
2004-01-01
Author
Özenbaş, Ahmet Macit
Metadata
Show full item record
Item Usage Stats
161
views
0
downloads
Cite This
In this work, TiO2 thin films were prepared by using sol-gel processing on soda-lime glass and silicon substrates. Precursor solutions for TiO2 films were prepared by using the proper amounts of titaniumtetraisopropoxide, diethanolamine and ethanol. The thickness of the TiO2 films was adjusted by repeating the spin coating cycle before the final heat treatment. Finally, various amounts of polyethylene glycol (PEG) were added to the above solution to observe its effect on the film morphology. The electrical characteristics were determined by using C-V measurements and respective dielectric constants were calculated. Results indicate that capacitance and the dielectric constant values of TiO2 films were comparable with the literature results and for 2.7 μm film thickness, dielectric constant was 24.
URI
https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=8644282087&origin=inward
https://hdl.handle.net/11511/82038
Collections
Unclassified, Article
Suggestions
OpenMETU
Core
Characterization of TiO2 thin films prepared by sol-gel processing
Özenbaş, Ahmet Macit (2004-01-01)
In this work, TiO2 thin films were prepared by using sol-gel processing on soda-lime glass and silicon substrates. Precursor solutions for TiO2 films were prepared by using the proper amounts of titaniumtetraisopropoxide, diethanolamine and ethanol. The thickness of the TiO2 films was adjusted by repeating the spin coating cycle before the final heat treatment. Finally, various amounts of polyethylene glycol (PEG) were added to the above solution to observe its effect on the film morphology. The electrical ...
Characterization of maghemite thin films prepared by sol-gel processing
Karakuşçu, Aylin; Özenbaş, Ahmet Macit; Department of Metallurgical and Materials Engineering (2006)
In this study, maghemite (γ-Fe2O3) thin films were prepared by chemical solution deposition on glass and quartz substrates. The solution was prepared by using 0.3 M iron (III) nitrate [Fe(NO3)3 - 9H2O] as precursor and dissolved in a mixture of 2-methoxyethanol and acetylacetone in a molar ratio of 20:2, by stirring the solution at RT for 2 hours. Substrates were prepared by either piranha etching method or ultrasonic cleaning method. The solution was spin coated on glass and quartz substrates at 1400 and 4...
Characterization and preparation of thin films and homogeneously precipitated Pb(Zr,Ti)O3 powders Homojen olarak çökelti̇lmi̇ş Pb(Zr,Ti)O3 tozlarin ve i̇nce fi̇lmleri̇n hazirlanmasi ve karakteri̇zasyonu
Özenbaş, Ahmet Macit (1999-12-01)
In this study, ferroelectric Pb(Zr,Ti)O3 powders and thin films were prepared from metal chlorides using sol-gel processing method. For powders; homogeneous precipitation from aqueous solution and for films; dip coating just before precipitation was applied in the presence of urea, [(NH2)2CO]. Characterization of the films and powders were carried out primarily by XRD and SEM/EDX. Both the films and powders were stoichiometric and completely crystallized into perovskite phase after annealing for 5 hours at ...
Synthesis of CNT-titania-silica nanocomposite thin films: the effect of heat treatment on photocatalytic activity
Kırbaş, Tuğçe; Doğu, Timur; Department of Chemical Engineering (2014)
In this study, CNT-TiO2-SiO2 nanocomposites were synthesized by sol-gel process and the thin films over glass substrates were fabricated by dip coating method. The effects of CNT addition, heat treatment temperature and atmospheres on the structure and photocatalytic properties were examined. The thin films were prepared with and without carbon nanotubes and the heat treatment was carried out at different temperatures in the range of 300-600oC under air and nitrogen atmosphere. Characterization of the sampl...
Synthesis of colloidal silver particles with different sizes by seeding approach for surface enhanced raman scattering (sers) studies
Sancı, Rukiye; Volkan, Mürvet; Department of Chemistry (2009)
In this study, silver nanorods and nanospheroids were prepared both in aqueous solution and on the surface of glass slides through seed-mediated growth approach at room temperature and used as a surface enhanced Raman scattering (SERS) substrate. The synthesis of metallic nanorods was started with the production of silver nanospheres as seed utilizing sodium borohydride and trisodium citrate as reducing and capping agents, respectively. These seeds were then added to a growth solution containing additional ...