Zn1-xCuxO thin films for NO gas detection deposited by SILAR method

2017-10-29
Karaduman, Irmak
Çorlu, Tuğba
Galioğlu, Sezin
Akata Kurç, Burcu
Yıldırım, Memet Ali
Ateş, Aytünç
Acar, Selim
NANOTR 13, (22 - 25 Ekim 2017)

Suggestions

Zn doped CaP coatings used for controlling the degradation rate of MgCa1 alloy: In vitro anticorrosive properties, sterilization and bacteria/cell-material interactions
Schmidt, Jürgen; Pana, Iulian; Bystrova, Anna; Dinu, Mihaela; Dekhtyar, Yuri; Vitelaru, Catalin; Gorohovs, Marks; Marinescu, Ioana Maria; HURİ, PINAR; Tamay, Dilara Goksu; Juravlea, Gabriela Andreea; Buyuksungur, Senem; Parau, Anca Constantina; Hasırcı, Vasıf Nejat; Hasırcı, Nesrin; Vladescu, Alina (2023-02-01)
The purpose of this study was to investigate the effect of Zn doped CaP coatings prepared by micro-arc oxidation method, as a possible approach to control MgCa1 alloy degradation. All the prepared coatings comprised a calcium deficient CaP phase. The control in this evaluation was performed with undoped CaP coating in SBF solution at body temperature (37 ± 0.5⁰C). The investigation involved determination of microchemical, mechanical, morphological, properties along with anticorrosive, cytocompatibility and ...
ZnO Nanorods as Antireflective Coatings for Industrial-Scale Single-Crystalline Silicon Solar Cells
AURANG, Pantea; Demircioglu, Olgu; ES, FIRAT; Turan, Raşit; Ünalan, Hüsnü Emrah (Wiley, 2013-04-01)
In this work, both planar and textured, industrial scale (156mmx156mm) single-crystalline silicon (Si) solar cells have been fabricated using zinc oxide (ZnO) nanorods as antireflection coating (ARC). ZnO nanorods were grown in a few minutes via hydrothermal method within a commercially available microwave oven. Relative improvement in excess of 65% in the reflectivity was observed for both planar and textured Si surfaces. Through ZnO nanorods, effective lifetime (eff) measurements were presented to investi...
ZnO varistors with iron oxide
Çam, İbrahim; Timuçin, Muharrem; Department of Metallurgical Engineering (1989)
ZnO quantum dots-graphene composites: Formation mechanism and enhanced photocatalytic activity for degradation of methyl orange dye
Tayyebi, Ahmad; Outokesh, Mohammad; Tayebi, Meysam; Shafikhani, Azizollah; Şengör, Sema Sevinç (2016-04-01)
The current study demonstrates homogenous decorating of zinc oxide quantum dots (QDs) onto graphene oxide (GO) surface via simple chemical method. The AFM image exhibited that the prepared graphene was 0.8 nm thick and hence practically monolayer. Average size of the ZnO QDs was estimated by transmission electron microscopy around 3 nm. Instrumental and chemical analyses demonstrated formation of a strong bond between ZnO QDs and GO, through C-O-Zn and C-Zn bridges. The UV-visible spectra displayed that the...
Zn-doped hydroxyapatite in biomedical applications
Uysal, Idil; Yilmaz, Bengi; Evis, Zafer (2021-03-01)
Hydroxyapatite, (Ca-10(PO4)(6)(OH)(2)), is a ceramic material similar to the inorganic part of the bone and can be synthesized in a laboratory environment with different methods. The structure of HA enables ionic substitutions that change its characteristics especially in terms of biological, antibacterial, and mechanical properties. Among the ions doped into HA structure, zinc (Zn), an essential trace element in the body, is also an important dopant for biomedical applications due to its positive effect on...
Citation Formats
I. Karaduman et al., “Zn1-xCuxO thin films for NO gas detection deposited by SILAR method,” 2017, p. 353, Accessed: 00, 2021. [Online]. Available: https://hdl.handle.net/11511/85250.