Effect of post fabrication aging treatment on the microstructure, crystallographic texture and elevated temperature mechanical properties of IN718 alloy fabricated by selective laser melting

Date

2022-08-01

Author

Ozer, Seren
Bilgin, Güney Mert
Davut, Kemal
Esen, Ziya
Dericioğlu, Arcan Fehmi

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

211
views

0
downloads

© 2022 Elsevier B.V.The effect of building direction and post fabrication aging treatment on the microstructure, crystallographic texture and high temperature mechanical properties of Inconel 718 (IN718) alloy fabricated by selective laser melting (SLM) method was investigated. After aging, arc-shaped structures seen in as-fabricated samples disappeared and converted into a mixture of columnar and equiaxed grains. Nano-sized γ″ and/or γ′ precipitates were formed upon aging; however, MC type carbides and Laves phase encountered in as-fabricated samples were not dissolved completely after aging. Moreover, aging did not alter the texture ((001)//building direction (BD)) of as-fabricated samples. Mechanical properties of the alloys under tension were influenced by the build direction, aging time and test temperature. As-fabricated samples produced in vertical direction exhibited higher room temperature strengths with lower ductility due to orientation of overlapped prior melt pools. Room temperature tensile test results revealed that peak aging caused a significant improvement in ultimate tensile strength (UTS), from 1066.5 MPa and 998.4 MPa to 1408.5 MPa and 1330.4 MPa whereas elongation values decreased from 27.5% and 32.2% to 19.6% and 23.7% in vertically and horizontally built samples, respectively. Peak-aged samples (aged at 700 °C for 8 h) tested at 600 °C displayed serrated regions in their stress-strain curves due to dynamic strain aging (DSA). Although strength values of the samples displayed an expected decrease by temperature, ductility of the samples reduced to minimum at temperatures around 700–800 °C, which was attributed to intermediate temperature embrittlement.

Subject Keywords

Additive manufacturing, Dynamic strain aging, Inconel 718 alloy, Mechanical properties, Selective laser melting, Texture

URI

https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85129768679&origin=inward
https://hdl.handle.net/11511/97586

Journal

Journal of Materials Processing Technology

DOI

https://doi.org/10.1016/j.jmatprotec.2022.117622

Collections

Department of Metallurgical and Materials Engineering, Article

Suggestions

OpenMETU
Core

Effect of post-processing heat treatment on the mechanical properties of inconel 718 fabricated by selective laser melting Özer, Seren; Dericioğlu, Arcan Fehmi; Department of Metallurgical and Materials Engineering (2020) In this study, effect of the building direction and post-processing heat treatments on the microstructure and high temperature mechanical properties of as-fabricatedInconel 718 alloys have been investigated. Inconel 718 samples were fabricated in two different building directions such that their longitudinalaxes wereeither parallel (horizontally built) or perpendicular (vertically built) to the building plate. During the selective laser melting (SLM)process, some undesired features can...
Effect of expandable graphite on flame retardant, thermal and mechanical properties of thermoplastic polyurethane composites filled with huntite&hydromagnesite mineral Guler, Turkan; Tayfun, Umit; Bayramlı, Erdal; DOĞAN, Mehmet (2017-01-10) The effect of expandable graphite (EG) was studied on the flame retardant, thermal and mechanical properties of thermoplastic polyurethane (TPU) containing huntite&hydromagnesite (HH). According to the flammability tests results, the synergistic interaction was observed between HH and EG. The maximum limiting oxygen index (LOI value was observed at a ratio of 1:1 (HH:EG) and the highest vertical burning test (UL-94) rating of V0 was observed at a ratios of 4:1, 3:2 and 1:1. The synergistic interaction betwe...
Optimization of the mechanical properties of Ti-6Al-4V alloy fabricated by selective laser melting using thermohydrogen processes BILGIN, Guney Mert; Esen, Ziya; Akin, Seniz Kushan; Dericioğlu, Arcan Fehmi (2017-07-17) 2-step Thermo Hydrogen Process (THP) including hydrogenation and dehydrogenation steps was applied to Ti-6Al-4V alloy fabricated by selective laser melting (SLM) process to refine the microstructure and to increase the ductility of the alloy. It was observed that as-fabricated alloy's surface was composed of oxides of titanium and aluminum, which may alter the hydrogenation kinetics. The hydrogen treatment for 1 hat 650 degrees C, the maximum hydrogen solubility temperature of the alloy, transformed startin...
Effect of CNT impregnation on the mechanical and thermal properties of C/C-SiC composites Tulbez, Simge; ESEN, ZİYA; Dericioğlu, Arcan Fehmi (2020-06-01) The present study investigates the effect of additional carbon source, in the form of carbon nanotubes (CNTs), on mechanical and thermal properties of carbon fiber reinforced silicon carbide (C/C-SiC) ceramic matrix composites (CMC) produced by liquid silicon infiltration (LSI) technique. The CNTs used in this study were impregnated into the C/C preforms before the liquid silicon infiltration stage. The results showed that the addition of excess carbon to the C/C preforms in the form of CNTs enhanced Si inf...
Effect of carbon nanotube surface treatment on the morphology, electrical, and mechanical properties of the microfiber-reinforced polyethylene/poly(ethylene terephthalate)/carbon nanotube composites Yesil, Sertan; Bayram, Göknur (2013-01-15) The aim of this study is to investigate the effects of carbon nanotube (CNT) chemical properties, CNT content, and molding temperature on the morphology, electrical, and mechanical properties of the microfiber-reinforced polymer composites. These composites were prepared by extrusion and hot stretching the poly(ethylene terephthalate) (PET)/CNT phase in high density polyethylene (HDPE) matrix. Surfaces of the CNT were modified by purification with strong acid mixture (HNO3 : H2SO4 mixture 1 : 1 by volume) f...

Citation Formats

S. Ozer, G. M. Bilgin, K. Davut, Z. Esen, and A. F. Dericioğlu, “Effect of post fabrication aging treatment on the microstructure, crystallographic texture and elevated temperature mechanical properties of IN718 alloy fabricated by selective laser melting,” Journal of Materials Processing Technology, vol. 306, pp. 0–0, 2022, Accessed: 00, 2022. [Online]. Available: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85129768679&origin=inward.