Microstructure and mechanical properties of squeeze cast intermetallic magnesium silicide dispersed aluminum-silicon-magnesium alloys

Download

068556.pdf

Date

1997

Author

Soyer, Önder Muzaffer

Metadata

Show full item record

Item Usage Stats

157
views

0
downloads

URI

https://hdl.handle.net/11511/1536

Collections

Graduate School of Natural and Applied Sciences, Thesis

Suggestions

OpenMETU
Core

Microstructure and corrosion characteristics of nickelless stainless steels Mehrabov, Amdulla; Aivazov, Bilayet; Aliyev, Maksut (2002-06-01)
Microstructural characterization and tensile properties of hot pressed Al-SiC composites prepared from pure Al and Cu powders Ögel, Bilgehan; Gürbüz, Rıza (2001-03-31) A conventional hot pressing method was used to produce Al-Cu-SiC particulate metal matrix composites. The matrix alloy was prepared from elemental powders of Al and 5 wt.% Cu. The composite comprises 13.3 or 27.2 vol.% SiCp with an average size of 10 mum. The powder mixtures were hot pressed uniaxially under nitrogen atmosphere. It is shown that Cu aids in the Formation of a liquid phase. Practically pore free structures are obtained after pressing at 600 degreesC, Elastic modulus, tensile strength and yiel...
Microstructure, phase relationships and microhardness of Fe60Al40-nHfn alloys (n=1, 3, and 5 at.%) Yildirim, Mehmet; Cetinbakis, Nese; Culu, Ayse; Akdeniz, Mahmut Vedat; Mehrabov, Amdulla (2021-04-01) The microstructural evolution, solidification behavior, phase relationships, microhardness and room temperature magnetic properties of the hypoeutectic Fe60Al40-nHfn (n = 1, 3, and 5 at.%) compositions are investigated in detail. The microstructure of the studied alloys is composed of Fe-Al based dendrites and eutectic mixture. The components of the eutectic are B2 Fe-Al based and HfFe6Al6 tau(1) phases. With increasing Hf fraction, the amounts of eutectic and tau(1) phases increase continuously which resul...
Microstructure, resistivity, and shear strength of electrically conductive adhesives made of silver-coated copper powder Hamrah, Z. Sahebi; Lashgari, V. A.; Mohammadi, M. H. Doost; Üner, Deniz; Pourabdoli, M. (2021-12-01) Electrically conductive adhesives were made using silver-coated copper powders (filler) and epoxy. Resistivity, microstructure and shear strength of prepared adhesives were studied using two-point resistance measurements, Scanning Electron Microscope (SEM) and universal tensile tests, respectively. Effect of filler concentration (70-85 wt%), silver concentration (10-50 wt%), particles morphology (flake or spherical) and addition of graphite (2-15 wt%) were investigated on prepared adhesives properties. Resu...
Microstructural evolution and room-temperature mechanical properties of as-cast and heat-treated Fe50Al50-nNbn alloys (n=1, 3, 5, 7, and 9 at%) Yıldırım, Mehmet; Akdeniz, Mahmut Vedat; Mehrabov, Amdulla (2016-05-10) The microstructural evolution and room-temperature mechanical properties of Fe50Al50-nNbn alloys (n=1, 3, 5, 7, and 9 at%) were investigated after solidification and subsequent heat treatment. For all the compositions, the (Fe, Al)(2)Nb Laves phase formed because of the incomplete solid solubility of Nb in the Fe-Al-based phases and tended to develop an eutectic mixture with the Fe-Al-based phase. According to the results of EDS analysis and microstructural investigations, the Nb concentration of the eutect...

Citation Formats

Ö. M. Soyer, “Microstructure and mechanical properties of squeeze cast intermetallic magnesium silicide dispersed aluminum-silicon-magnesium alloys,” Middle East Technical University, 1997.