Reactive processing and characterization of anhydride/hydroxyl and anhydride/epoxy functionalized blends

Download
082451.pdf
1999
Bayram, Göknur
Show full item record
133
views
0
downloads
Polymers, Polymer liquid crystals, Anhydrides
https://hdl.handle.net/11511/2496
Graduate School of Natural and Applied Sciences, Thesis

Suggestions

Thermal characterization of phenol and bisphenol-A based polybenzoxazines
Bagherifam, Shahla; Hacaloğlu, Jale; Department of Polymer Science and Technology (2009)
Although, several researches on synthesis and characterization of benzoxazines and polybenzoxazines have appeared in the literature, detailed studies on thermal characterization are still limited. In this study, polymerization and thermal degradation mechanisms of benzoxazines were investigated via direct pyrolysis mass spectrometry. Benzoxazine monomers prepared by reactions of phenol or bisphenol- A with aniline or methyl amine were analyzed to investigate the effects of the structures of phenyl and amine...
Impact modified polyamide-organoclay nanocomposites
Işık, Işıl; Yılmazer, Ülkü; Department of Chemical Engineering (2007)
The effects of melt state compounding and addition order of ethylene-butyl acrylate-maleic anhydride (E-BA-MAH), ethylene-glycidyl methacrylate (E-GMA), ethylene-methyl acrylate-glycidyl methacrylate (E-MA-GMA) terpolymer and/or three types of organoclays (Cloisite® 15A, 25A and 30B) on morphology, thermal, mechanical and dynamic mechanical properties of polyamide-6 are investigated. XRD patterns show that the interlayer spacing for Cloisite® 15A remained unchanged; however it increased for the organoclays ...
Flame retardancy of polyamide compounds and micro/nano composites
Gündüz, Hüseyin Özgür; Kaynak, Cevdet; Department of Polymer Science and Technology (2009)
In the first part of this dissertation, glass fiber reinforced/unreinforced polyamide 6 (PA6) and polyamide 66 (PA66) were compounded with three different flame retardants, which were melamine cyanurate, red phosphorus and brominated epoxy with antimony trioxide, by using an industrial scale twin screw extruder. Then, to investigate flame retardancy of these specimens, UL-94, Limiting Oxygen Index (LOI) and Mass Loss Cone Calorimeter (MLC) tests were carried out. In addition to flammability tests, thermogra...
Polymerization and polymer characterization of n-vinylcaprolactam
Polat, Özlem; Usanmaz, Ali; Department of Polymer Science and Technology (2005)
In this study, N-vinylcaprolactam was polymerized by radiation in the solid state. The polymerization was carried out at room temperayure under vacuum and open to atmosphere respectively. The polymerization mechanism showed autoacceleration and the rate of polymerization was higher in the presence of oxygen. However the limiting conversion was 100% under vacuum conditions and 90% in the present of oxygen. This is due to the low molecular weight olgomer formation in the presence of oxygen. The polymers were ...
Spray coatable electrochromic dioxythiophene polymers with high coloration efficiencies
REEVES, Benjamin D.; GRENIER, Christophe R.G.; ARGUN, Avni A.; Çırpan, Ali; MCCARLEY, Tracy D.; REYNOLDS, John R. (2004-10-05)
Four new disubstituted propylenedioxythiophene polymers have been synthesized by Grignard metathesis on the 1-5 g scale. All polymers were found to be soluble in chloroform, methylene chloride, toluene, and tetrahydrofuran and were fully structurally characterized having GPC determined number-average molecular weights ranging from 33000 to 47000 g mol(-1). Dilute polymer solutions in toluene exhibited strong red fluorescence with moderate quantum efficiencies from 0.38 to 0.50. Homogeneous thin films were f...
Citation Formats
G. Bayram, “Reactive processing and characterization of anhydride/hydroxyl and anhydride/epoxy functionalized blends,” Ph.D. - Doctoral Program, Middle East Technical University, 1999.
METU IIS - Integrated Information Service open@metu.edu.tr