EXPERIMENTAL INVESTIGATION OF FATIGUE DAMAGE ACCUMULATION IN 1100-AL ALLOY

Date

1991-01-01

Author

BILIR, OG

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

283
views

0
downloads

The cumulative fatigue damage characteristics of 1100 Al alloy were studied to gain a better understanding of the effects of the loading sequence, the percentage of initial applied load cycles and the stress ratio.

Subject Keywords

Mechanical Engineering, Modelling and Simulation, Industrial and Manufacturing Engineering, General Materials Science, Mechanics of Materials

URI

https://hdl.handle.net/11511/64249

Journal

INTERNATIONAL JOURNAL OF FATIGUE

DOI

https://doi.org/10.1016/0142-1123(91)90122-f

Collections

Department of Mechanical Engineering, Article

Suggestions

OpenMETU
Core

A CRITIQUE ON FATIGUE CRACK-GROWTH LIFE ESTIMATION METHODOLOGIES AKYUREK, T; BILIR, OG (Elsevier BV, 1992-01-01) In this study, three fatigue crack growth life estimation methodologies are reviewed and sample calculations are made using these methodologies. Comparison of the results with respect to the methodologies are made. Three computer codes which represent these methodologies, CRACKS IV, FASTRAN and FATIGUE are selected for the analyses. The estimations are also correlated to the test results found in the literature. FALSTAFF spectra are used in the analyses.
Crack path and life prediction under mixed mode cyclic variable amplitude loading through XFEM Dirik, Haydar; Yalçınkaya, Tuncay (Elsevier BV, 2018-09-01) In the present paper, a mesh independent computational algorithm is developed and incorporated into a commercial finite element software (Abaqus) for automated fatigue crack growth analysis under mixed mode variable amplitude loading conditions. The algorithm calculates the stress intensity factor (SIF) at predetermined small crack growth increments in the finite element software by using Extended Finite Element Method (XFEM) and predict the fatigue crack growth (FCG) path through local symmetry (K-II = 0) ...
Experimental investigation of residual stresses introduced via shot peening and their effect on fatigue life of ball bearings Küçükyılmaz, Ali; Gür, Cemil Hakan; Department of Metallurgical and Materials Engineering (2010) In this study, residual stresses introduced via application of shot peening on the raceways of bearing rings and their effect on the fatigue life was investigated experimentally. For improvement of residual compressive stress state, shot peening operation with different parameters was utilized. Residual stress measurements were conducted via X-ray diffraction technique. Optimization of residual stress state during the production of ball bearings is the main target of this study. Process parameters for shot ...
Effect of microstructural modification on damage tolerance of 34CrMo4 shaft steel Ozcan, Burak; Gurer, Goksu; Gür, Cemil Hakan (Wiley, 2020-06-01) Overall damage tolerances of the heat-treated 34CrMo4 steels having ferritic-pearlitic, bainitic, and tempered-martensitic microstructures were evaluated based on their threshold stress intensity factor prior to small crack propagation, fatigue strength, and fracture toughness under static loading. Kitagawa-Takahashi diagrams were constructed to determine the limiting size of small crack propagation. The micromechanical effects of carbide morphology and phase distribution on quasi-static and dynamic mechani...
EXPERIMENTAL ANALYSIS AND TRANSIENT SIMULATION OF HEAT TRANSFER INSIDE THE FINNED TUBE ADSORBENT BED OF A THERMAL WAVE CYCLE ÇAĞLAR, AHMET; Yamali, Cemil (Begell House, 2019-01-01) Heat transfer enhancement inside the adsorbent bed of a thermal wave adsorption cooling cycle is investigated both experimentally and theoretically. Various adsorbent materials are tested using a finned tube adsorbent bed for the thermal wave cycle. The mathematical model is well defined, including a 2-D coupled heat and mass transfer analysis. This study presents the effects of heat transfer fluid velocity, regeneration temperature, condenser pressure, and particle diameter on the heat transfer enhancement...

Citation Formats

O. BILIR, “EXPERIMENTAL INVESTIGATION OF FATIGUE DAMAGE ACCUMULATION IN 1100-AL ALLOY,” INTERNATIONAL JOURNAL OF FATIGUE, pp. 3–6, 1991, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/64249.