Secondary Growth of Microporous Vanadosilicate AM 6 Films

Kuzyaka, Duygu
Galioglu, Sezin
Akata Kurç, Burcu
18th International Zeolite Conference, (19 - 24 Haziran 2016)


Kuzyaka, Duygu; Sezin, Galioglu; Akata Kurç, Burcu (2015-09-15)
Secondary growth of microporous vanadosilicate AM-6 films
Kuzyaka, Duygu; Galioglu, Sezin; Akata Kurç, Burcu (2016-10-01)
Oriented vanadosilicate AM-6 thin films with an average thickness of 1-2 mu m were prepared on the ITO coated glass substrates using secondary growth method with a partial a(b)-out-of-plane preferred crystal orientation for the first time. In secondary growth method, titanosilicate ETS-10 crystals were deposited on the substrate from a colloidal suspension to form seed layers. Then, the hydrothermal growth of the seed crystals was conducted to form AM-6 films. It was observed that the AM-6 films formed poss...
Direct growth of type II InAs/GaSb superlattice MWIR photodetector on GaAs substrate
SERİNCAN, UĞUR; Arikan, Bulent; Senel, Onur (Elsevier BV, 2018-08-01)
We report on the direct growth and characterization of type-II InAs/GaSb superlattice (T2SL) MWIR photodetector structure grown on a GaAs substrate by molecular beam epitaxy. The designed photodetector structure contains 140 period of 8.0 ML InAs/8.3 ML GaSb p-i-n SL structure with a 50% cutoff wavelength of 3.78 pm. We achieved a peak specific detectivity (D*) and differential resistance area product at zero bias (R(0)A) of 1.3 x 10(12)cm Hz(1/2) W-1 and 10(4) Omega cm(2) at 80 K, respectively. The obtaine...
HOWARD, AG; Volkan, Mürvet; Ataman, Osman Yavuz (1987-02-01)
A surface-modified silica gel has been developed for the pre-concentration of arsenite from natural waters. The reaction of silica gel with (3-mercaptopropyl)trimethoxysilane produces a mercapto-modified silica gel with a silver capacity of ca. 0.9 mmol g–1. This material selectively removes arsenite from samples that also contain arsenate, monomethylarsonate and dimethylarsinate, and can be employed for both the column and batch pre-concentration of arsenite. Under column and batch conditions recoveries of...
Secondary structure and conformational change of mushroom polyphenol oxidase during thermosonication treatment by using FTIR spectroscopy
Baltacıoğlu, Hande; Bayındırlı, Alev; Severcan, Feride (2017-01-01)
To understand the conformational changes of mushroom PPO, the secondary structural change of the enzyme during thermosonication treatment at different power (60, 80 and 100%), temperature (20-60 degrees C) and time (0-30 min) combinations was investigated by using FTIR spectroscopy and compared with the change in enzyme activity. The enzyme inactivation higher than 99% was obtained at 100% amplitude at 60 degrees C for 10 min. FTIR studies showed that marked spectral changes were noted after ultrasound trea...
Citation Formats
D. Kuzyaka, S. Galioglu, and B. Akata Kurç, “Secondary Growth of Microporous Vanadosilicate AM 6 Films,” presented at the 18th International Zeolite Conference, (19 - 24 Haziran 2016), Rio de Janeiro, Brazil, 2016, Accessed: 00, 2021. [Online]. Available: