Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Open Access Guideline
Open Access Guideline
Postgraduate Thesis Guideline
Postgraduate Thesis Guideline
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
Low-temperature visible photoluminescence spectra of TlGaSe2 layered crystal
Download
index.pdf
Date
2000-02-01
Author
Hasanlı, Nızamı
Aydinli, A
Baten, SMA
Metadata
Show full item record
This work is licensed under a
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License
.
Item Usage Stats
194
views
0
downloads
Cite This
The photoluminescence (PL) spectra of TlGaSe2 layered single crystals were investigated in the 8.5-35 K temperature, 0.2-15.2 W cm(-2) excitation laser intensity, and in the 600-700 nm wavelength range. The PL spectrum has a slightly asymmetric Gaussian lineshape with a peak position located at 1.937 eV (640 nm) at 8.5 K. The PL is quenched with increasing temperature. The blue shift of the PL peak and the sublinear increase of the PL intensity with increasing laser intensity is explained using the inhomogenously spaced donor-acceptor pair recombination model. Analysis of the data indicates that the PL band is due to donor-acceptor recombination. A shallow acceptor level and a moderately deep donor level are, respectively, introduced at 0.012 eV above the top of the valence band and ar 0.317 eV below the bottom of the conduction band. An energy-level diagram for radiative donor-acceptor pair recombination in TlGaSe2 layered single crystals is proposed
Subject Keywords
Semiconductors
,
Photoluminescence
,
Impurity level
,
TlGaSe2
URI
https://hdl.handle.net/11511/42080
Journal
JOURNAL OF LUMINESCENCE
DOI
https://doi.org/10.1016/s0022-2313(99)00174-x
Collections
Department of Physics, Article
Suggestions
OpenMETU
Core
Low-temperature visible photolummescence and optical absorption in Tl2In2Se3S semiconductor
Güler, Işıkhan; Hasanlı, Nızamı; Turan, Raşit (2007-05-31)
The emission band spectra of undoped T1(2)In(2)Se(3)S layered crystals have been studied in the temperature range of 25-63 K and the wavelength region of 570-700nm. A broad photoluminescence band centered at 633 nm (1.96 eV) was observed at T = 25 K. Variation of emission band has been studied as a function of excitation laser intensity in the 2.7-111.4mWcm(-2) range. Radiative transitions from shallow donor level located at 0.03 eV below the bottom of conduction band to deep acceptor level located at 0.23 ...
Defect characterization of cTl(4)GaIn(3)Se(2)S(6) layered single crystals by photoluminescence
Hasanlı, Nızamı (2015-10-01)
Photoluminescence (PL) spectra of Tl4GaIn3Se2S6 layered crystals grown by the Bridgman method have been studied in the energy region of 2.02-2.35 eV and in the temperature range of 16-45 K. A broad PL band centered at 2.20 eV was observed at T = 16 K. Variations of emission band has been studied as a function of excitation laser intensity in the 0.1 to 149.9 mW cm(-2) range. Radiative transitions from shallow donor level located at 10 meV below the bottom of conduction band to moderately deep acceptor level...
Low-temperature photoluminescence in CuIn5S8 single crystals
Hasanlı, Nızamı (2016-06-01)
Photoluminescence (PL) spectra of CuIn5S8 single crystals grown by Bridgman method have been studied in the wavelength region of 720-1020 nm and in the temperature range of 10-34 K. A broad PL band centred at 861 nm (1.44 eV) was observed at T = 10 K. Variations of emission band has been studied as a function of excitation laser intensity in the 0.5- 60.2 mW cm(-2) range. Radiative transitions from shallow donor level located at 17 meV below the bottom of the conduction band to the acceptor level located at...
Low-temperature photoluminescence spectra of InS single crystals
Hasanlı, Nızamı (1997-03-01)
Photoluminescence (PL) spectra of InS were investigated in the wavelength region 477.5-860 nm and in the temperature range 8.5-293 K. We observed three PL bands centered at 605 nm (A-band), 626 nm (B-band) and 820 nm (C-band). The A- and B-bands are due to radiative transitions hom the donor level at 0.01 eV below the bottom of the conduction band to the valence band and from the donor level at 0.06 eV below the bottom of the conduction band to the acceptor level 0.12 eV above the top of the valence band, r...
Donor-acceptor pair recombination in Tl2InGaS4 layered crystals
Goksen, K; Hasanlı, Nızamı; Ozkan, H; Aydinli, A (2005-08-01)
Photoluminescence (PL) spectra of Tl2InGaS4 layered single crystals were studied in the temperature range 15-150 K and wide laser excitation intensity range 0.01-110.34 Wcm(-2). We observed a total of three PL, bands, one centered at 542 nm (2.286 eV, A-band), one at 607 nm (2.041 eV, B-band), and one at 707 nm (1.754 eV, C-band), at various excitation intensities. The A- and the B-bands were determined to be due to radiative transitions from moderately deep donor levels located at 0.189 and 0.443 eV below ...
Citation Formats
IEEE
ACM
APA
CHICAGO
MLA
BibTeX
N. Hasanlı, A. Aydinli, and S. Baten, “Low-temperature visible photoluminescence spectra of TlGaSe2 layered crystal,”
JOURNAL OF LUMINESCENCE
, pp. 39–43, 2000, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/42080.